| Genus ferri | Chalybs formae: |
| Norma |
|
| Specificationes productionis | Lamina ferrea, Charta, Coil, Vectis plana, Vectis rotunda, Taenia ferrea, Filum, Omnia genera elementorum fabricatorum. |
| Machinatio | Vertens Fresatura Trituratio Foramen profundum: longitudo maxima 9.8 metra. |
| Ambitus laboris | Ferrum rotundum: 1mm ad 2000mm Chalybs quadratus: 10mm ad 1000mm Lamina/lamina ferrea: 0.08mm ad 800mm Latitudo: 10mm ad 1500mm Longitudo: Quamlibet longitudinem secundum desiderium emptoris praebere possumus. Fabricatio: Axes cum lateribus/tubis/tubis ligneis/torticulis/cubis/aliis formis Tubi: Diametros exteriores: φ4-410 mm, crassitudine parietis ab 1-35 mm variante. |
| Tractatio caloris | Normalizatio, recoctio, temperatio, restinguitio, induratio et temperatio, conditura, induratio superficialis, carburizatio |
AWS E10015-D2 COMPOSITIO CHEMICA ET PROPRIETATES MECHANICAE:
| C ≤ | Si ≤ | Mn ≤ | P ≤ | S ≤ | Cr | Ni |
| 0.15 | 0.6 | 1.65-2.0 | 0.03 | 0.03 | ≤0.9 | |
| Mo | Al | Cu | Nb | Ti | V | Ce |
| 0.25-0.45 | ||||||
| N | Co | Pb | B | Alia |
PROPRIETATES MECHANICAE:
| Proprietates | Conditiones | ||
| Temperatura (°C) | Curatio | ||
| Densitas (×1000 kg/m3) | 7.7-8.03 | 25 |
|
| Ratio Poissoniana | 0.27-0.30 | 25 |
|
| Modulus Elasticus (GPa) | 190-210 | 25 |
|
| Robur Tensilis (Mpa) | 1158 | 25 | oleo extinctum, granis subtilibus, temperatum ad 425°C |
| Robur Cedendi (Mpa) | 1034 | ||
| Elongatio (%) | 15 | ||
| Reductio in Area (%) | 53 | ||
| Duritia (HB) | 335 | 25 | oleo extinctum, granis subtilibus, temperatum ad 425°C |
| Proprietates | Conditiones | ||
| Temperatura (°C) | Curatio | ||
| Conductivitas Thermalis (W/mK) | 42.7 | centum | |
| Calor Specificus (J/kg-K) | 477 | 50-100 | |
PROPRIETATES PHYSICAE:
| Quantitas | Valor | Unitas |
| Expansio thermalis | XVI-XVII | e-6/K |
| Conductivitas thermalis | XVI - XVI | W/mK |
| Calor specificus | 500 - 500 | J/kg.K |
| Temperatura liquefactionis | 1370 - 1400 | °C |
| Temperatura servitii | 0 - 500 | °C |
| Densitas | 8000 - 8000 | kg/m³ |
| Resistivitas | 0.7 - 0.7 | Ohm.mm²/m |
E7015-G Electroda Soldandi Tegumentis Natrii Humilis Hydrogenii
DESCRIPTIO:
Virga ferrea ad soldandum est, quae temperaturae humilis est, obducta cum hydrogeno sodio humili, niccolo continente. Soldatio plenae positionis per nexum inversum DC fieri potest. Metallum ad soldandum, temperatura -80°C, bonam tenacitatem contra impetum retinet.
USUS:
Structura ferrea 1.5Ni, ad -80°C operans, sudanda.
COMPOSITIO CHEMICA METALLI DEPOSITI:
| C | Mn | Si | Ni | S | P | |
| Norma | ≤0.08 | ≤1.25 | ≤0.60 | ≥1.00 | ≤0.035 | ≤0.035 |
| Experimentum | 0.045 | 0.60 | 0.27 | 1.80 | 0.010 | 0.015 |
EFFECTUS MECHANICUS METALLI DEPOSITI:
| Robur tensile Rm (MPa) | Robur Cedendi Rel (MPa) | Elongatio A (%) | -80°C Valor Impactus Akv (J) | |
| Norma | ≥490 | ≥390 | ≥22 | ≥27 |
| Experimentum | 530 | 445 | 30 | centum |
CURSUS REFERENTIALIS (DC+):
| Diameter (mm) | 3.2 | 4.0 | 5.0 | |
| Longitudo (mm) | 350 | quadringenti | quadringenti | |
| Currens (A) | 90-120 | 140-180 | CLXXX-CCX |
| E12015-G | Secundum GB E8515-G Correspondens cum AWS E12015-G |
Introductio: E12015-G est genus electrodi chalybis humilis mixturae altae firmitatis, cum indumento generis natrii humilis hydrogenii. DCRP (Polaritas Inversa Currentis Directi). Soldatura omnibus positionibus.
Usus: Ad structuras chalybis humiliter mixti et altae firmitatis cum robore tensile circiter 830MPa soldandas adhibitus est.
Compositio Chemica Metalli Depositi (%)
| Compositio Chemica | C | Mn | Si | S | P | Mo |
| Valor Garantiae | ≤0.15 | ≥1.00 | 0.4~0.8 | ≤0.035 | ≤0.035 | 0.60~1.20 |
| Resultatum Generale | ≤0.10 | ~1.50 | ≤0.70 | ≤0.020 | ≤0.020 | ~0.90 |
Proprietates Mechanicae Metalli Depositi
| Res Probationis | Rm(MPa) | ReL velRp0.2(Mpa) | A(%) | KV2(I) |
| Valor Garantiae | ≥830 | ≥740 | ≥12 | —(temperatura normalis) |
| Resultatum Generale | 860~950 | ≥750 | XII~XX | ≥27 |
Contentum Hydrogenii Diffusibilis in Metallo Deposito: ≤5.0ml/100g (Chromatographia)
Inspectio Radiographica X-Ray: Gradus I
INSTRUCTIONES:
1. Electroda ante soldaduram sub 350-400℃ per horam coquenda sunt, deinde in pyxidem insulationis ponenda et quam primum opus est adhibenda.
2. Maculae in sutura, ut rubigo, removendae sunt, et sutura ad circiter 200°C prae calefacienda est.
3. Coniunctio sub 600-650℃ post coniunctionem temperari potest ut tensio interna eliminetur.
Producta Similia
-
AWS E7015-G Instrumentum Electricum ad Ferrum Soldandum Temperaturae Humilis...
-
Electrodum ferreum W707Ni temperaturae humilis ...
-
AWS E8018-C1 Electrica ad Ferrum Soldandum Temperaturae Humilis...
-
AWS E7015-C2L Electrica ad Ferrum Soldandum Temperaturae Humilis...
-
AWS E7015-G Instrumentum Electricum ad Ferrum Soldandum Temperaturae Humilis...